RDT1320 Carbon Steel Strip
Rebo RDT1320 is a dual phase carbon steel strip containing 75% martensite and 25% ferrite matrix. Its surface is smooth, hard, with a gray oxide layer, low corrosion risk of any application can be applied.
Tensile strength：1340 Mpa
Yield strength：1250 Mpa
Fatigue Strength：410 Mpa
Hardness：36±1 HRC
Elongation：4%
Weld factor：0.75
Rebo RDT1320 is a dual phase carbon steel strip containing 75% martensite and 25% ferrite matrix. Its surface is smooth, hard, with a gray oxide layer, low corrosion risk of any application can be applied. Excellent thermal conductivity makes it ideal for baking and similar applications. Its low carbon content makes it unnecessary to temper after welding.
|
C |
Si |
Mn |
Al |
Nb |
Fe |
|
0.15 |
0.5 |
1.8 |
0.04 |
0.03 |
- |
Static Strength
Standard strength at room temperature (nominal values)
|
Parametric |
Tensile strength |
Yield strength |
Elongation |
Weld factor |
Hardness |
|
|
Mpa |
Mpa |
A5(%) |
Rm/Rm |
HRC |
|
Base material |
1340 |
1250 |
5 |
· |
36±1 |
|
Welding area |
1000 |
890 |
4 |
0.75 |
· |
| Length |
Customizable |
| Width |
800/1000/1200/…mm |
| Thickness |
0.8/1.2/1.4/1.5mm |
| Note | The Rebo steel strip comes in a width of 1200mm, but can be customized to different sizes through cutting or longitudinal welding. |
- Great static strength
- Excellent wear resistance
- Excellent fatigue strength
- Good repairability
- Great thermal properties
- Wood based panel industry
- Food industry
- Transportation industry
- Other industries